What is Polyamide 66 plastic? PA66 melting point 260~265℃, glass transition temperature (dry state) is 50℃. Density is 1.13~1.16 g/cm3.PA66 has low water absorption, excellent dimensional stability and high rigidity. Higher melting point, can be used for a long time in harsh environments, in a wide range of temperatures can still maintain sufficient stress, continuous use temperature of 105 ℃. Long glass fiber reinforced composite Glass fiber reinforced plastic is based on the original pure plastic, filling glass fibers and other additives, so as to improve the scope of use of the material. Generally speaking, most of the glass fiber reinforced materials are used in the structural parts of the products, which is a kind of structural engineering materials, such as: PP, ABS, PA66, PA6, TPU, PPA, PBT, PEEK, PBT, PPS and so on.Advantages1)After glass fiber reinforcement, glass fiber is a high temperature resistant material, therefore, the heat-resistant temperature of reinforced plastics is much higher than before without glass fiber, especially nylon plastics.2)After the glass fiber reinforcement, due to the addition of glass fiber, the plastic polymer chain is restricted to move with each other, therefore, the shrinkage of reinforced plastics decreases a lot, and the rigidity is greatly improved.3)After glass fiber reinforced, the reinforced plastic will not stress cracking, at the same time, the impact resistance of the plastic improves a lot.4)After the glass fiber reinforcement, the glass fiber is a high strength material, which also greatly improves the strength of the plastic, such as: tensile strength, compression strength, bending strength, improve a lot.5)After glass fiber reinforcement, due to the addition of glass fiber and other additives, the combustion performance of the reinforced plastics decreases a lot, most of the materials can not be ignited, it is a kind of flame-retardant material. Datasheet for reference Applications PA66's comprehensive performance is good, with high strength, good rigidity, impact resistance, oil and chemical resistance, abrasion resistance and self-lubricating advantages, especially hardness, rigidity, heat resistance and creep performance is better. Datails Grade Fiber specification Main characteristics Applications General grade 20%-60% high toughness (especially at low temperatures),excellent creep and fatigue resistance,low warpage Automobiles, electronic and electrical appliances, sports equipment, power tools, high-speed rail parts, etc. Toughen resistance grade 20%-50% high impact strength,light texture Automobiles, electronic appliances, sports equipment, power tools, tool handles, high-speed rail parts, gears, etc. Lab & Factory About company Xiamen LFT Composite Plastic Co., LTD wurde 2009 gegründet und ist ein weltweit tätiger Markenlieferant von langfaserverstärkten thermoplastischen Materialien, der Produktforschung und -entwicklung (F&E), Produktion und Verkaufsmarketing vereint. Unsere LFT-Produkte haben die Systemzertifizierung ISO9001 und 16949 bestanden und zahlreiche nationale Marken und Patente erhalten, die die Bereiche Automobil, Militärteile und Schusswaffen, Luft- und Raumfahrt, neue Energie, medizinische Geräte, Windenergie, Sportgeräte usw. abdecken.

Was ist TPU? TPU (Thermoplastisches Polyurethan) ist ein Elastomerkautschuk. Es wird hauptsächlich in Polyester- und Polyethertypen unterteilt, hat einen breiten Härtebereich (60HA-85HD), ist verschleißfest, ölbeständig, transparent und elastisch und wird häufig in Alltagsgegenständen, Sportartikeln, Spielzeugen, Dekorationsmaterialien und anderen Bereichen verwendet. Halogenfreies, flammhemmendes TPU kann auch Weich-PVC ersetzen, um immer mehr Umweltschutzanforderungen zu erfüllen. Der sogenannte elastische Körper bezieht sich auf eine Glasübergangstemperatur, die niedriger als die Raumtemperatur ist, eine Bruchdehnung von >50 %, und das Polymermaterial erholt sich nach dem Entfernen der äußeren Kraft gut. Polyurethanelastomer ist eine spezielle Kategorie von Elastomeren, der Härtebereich von Polyurethanelastomeren ist sehr breit und der Leistungsbereich ist sehr breit, sodass Polyurethanelastomer eine Art Polymermaterial zwischen Gummi und Kunststoff ist. Es kann durch Erhitzen plastifiziert werden und hat in seiner chemischen Struktur wenig oder keine Vernetzung. Seine Moleküle sind im Wesentlichen linear, aber es gibt eine gewisse physikalische Vernetzung. Diese Art von Polyurethan wird als TPU bezeichnet. Warum Langglasfaser verfüllen? Mit langen Glasfasern verstärkte Verbundwerkstoffe können Ihre Probleme lösen, wenn andere Methoden zur Verstärkung von Kunststoffen nicht die gewünschte Leistung erbringen oder wenn Sie Metall durch Kunststoff ersetzen möchten. Mit langen Glasfasern verstärkte Verbundwerkstoffe können die Kosten der Waren kostengünstig gesenkt und die mechanischen Eigenschaften technischer Polymere effektiv verbessert werden. Durch die Bildung langer Fasern zu einem langfaserverstärkten internen Skelettnetzwerk wird die Haltbarkeit erhöht. Die Leistung bleibt in einer Vielzahl von Umgebungen erhalten. Im Vergleich zu Kurzglasfaser Anwendung Autotüren und -fenster, Sicherheitskappen, mechanische Teile, Kästen für pneumatische Nagelpistolen, professionelle Elektrowerkzeuge, Schrauben und Muttern usw. Über uns Xiamen LFT Composite Plastic Co., Ltd. ist ein Markenunternehmen, das sich auf LFT und LFRT konzentriert. Long Glass Fiber Series (LGF) und Long Carbon Fiber Series (LCF). Das thermoplastische LFT des Unternehmens kann für LFT-G-Spritzguss und Extrusion sowie für LFT-D-Formgebung verwendet werden. Es kann nach Kundenwunsch hergestellt werden: 5 bis 25 mm lang. Die langfaserverstärkten, durch kontinuierliche Infiltration verstärkten Thermoplaste des Unternehmens haben die Systemzertifizierung ISO9001 und 16949 bestanden und die Produkte haben zahlreiche nationale Marken und Patente erhalten. Zertifizierung des Qualitätsmanagementsystems ISO9001 und 16949 Nationales Laborakkreditierungszertifikat Modifiziertes Kunststoff-Innovationsunternehmen Ehrenurkunde Schwermetall-REACH- und ROHS-Prüfung

PA6 material PA6 is one of the most widely used materials in the current field, and PA6 is a very good engineering plastic with balanced and good performance. The raw materials for the manufacture of nylon 6 engineering plastic are extensive and inexpensive, and it is not restricted by the technological monopoly of foreign companies.However, in order to make good use of this inexpensive and excellent material, we must first understand it. Today, we will start with glass fiber reinforced PA6 engineering plastics, because it is the most important category of PA6 engineering plastics.Just like any other engineering plastics, PA6 has advantages and disadvantages, such as high water absorption, low temperature impact toughness and dimensional stability is relatively poor. So engineers will use different methods to make PA6 better, which we call modification. At present, the most common method is to blend and modify PA6 with glass fiber (GF).Today, we will take a look at the mechanical properties of PA6 engineering plastics under the glass fiber GF system for reference and help us select materials. PA6-LGF 1. Influence of glass fiber content on PA6 engineering plastics We can find from the application and experiment that the content index is often one of the biggest influencing factors in fiber reinforced composites.As the glass fiber content increases, the number of glass fibers per unit area of the material will increase, which means that the PA6 matrix between the glass fibers will become thinner. This change determines the impact toughness, tensile strength, bending strength and other mechanical properties of glass fiber reinforced PA6 composites.In terms of impact performance, the increase of glass fiber content will greatly increase the notch impact strength of PA6. Taking long glass fiber (LGF) filling PA6 as an example, when the filling volume increases to 35%, the notch impact strength will increase from 24.8J/m to 128.5J/m. But the glass fiber content is not more is better, short glass fiber (SGF) filling volume reached 42%, the impact strength of the material reached the highest 17.4kJ/㎡, but continue to add will let the gap impact strength showed a downward trend.In terms of bending strength, the increase of the amount of glass fiber will make the bending stress can be transferred between the glass fiber through the resin layer; At the same time, when the glass fiber is extracted from the resin or broken, it will absorb a lot of energy, thus improving the bending strength of the material.The above theory is verified by experiments. The data show that the bending elastic modulus increases to 4.99GPa when the LGF (long glass fiber) is filled to 35%. When the content of SGF (short glass fiber) is 42%, the bending elastic modulus reaches 10410MPa, which is about 5 times that of pure PA6. 2. Influence of glass fiber retention length on PA6 composites The fiber length of the glass fiber also has an obvious effect on the mechanical properties of the material. When the length of the glass fiber is less than the critical length (the length of the fiber when the material has the tensile strength of the fiber), the interface binding area of the glass fiber and the resin increases with the increase of the length of the glass fiber. When the composite material is broken, the resistance of the glass fiber from the resin is also greater, so as to improve the ability to withstand the tensile load.When the length of glass fiber exceeds the critical, the longer glass fiber can absorb more impact energy under impact load. In addition, the end of the glass fiber is the initiation point of crack growth, and the number of long glass fiber ends is relatively less, and the impact strength can be significantly improved.The experimental results show that the tensile strength of the material increases from 154.8MPa to 164.4MPa when the glass fiber content is kept at 40% and the length of the glass fiber increases from 4mm to 13mm. The bending strength and notched impact strength increased by 24% and 28%, respectively.Moreover, the research shows that when the original length of the glass fiber is less than 7mm, the material performance increases more obviously. Compared with short glass fiber, long glass fiber reinforced PA6 material has better appearance warping resistance, and can better maintain mechanical properties under high temperature and humidity conditions. TDS for your reference PA6 can be made into long glass fiber reinforced material by adding 20%-60% long glass fiber according to the characteristics of the product. PA6 with long glass fiber added has better strength, heat resistance, impact resistance, dimensional stability and warping resistance than without glass fiber added. Following TDS show the data of PA6-LGF30. Application PA6-LGF has the largest proportion of applications in the automotive industry, by electronic and electrical applications, and also involving machinery and engineering parts. Aut...

Aufgrund seiner wünschenswerten Eigenschaften wird ABS häufig beim Spritzgießen verwendet.

PA6-Material PA6 ist eines der am häufigsten verwendeten Materialien auf diesem Gebiet und PA6 ist ein sehr guter technischer Kunststoff mit ausgewogener und guter Leistung. Die Rohstoffe für die Herstellung von technischen Kunststoffen aus Nylon 6 sind umfangreich und kostengünstig und werden nicht durch das Technologiemonopol ausländischer Unternehmen eingeschränkt. Um dieses kostengünstige und hervorragende Material jedoch sinnvoll nutzen zu können, müssen wir es zunächst verstehen. Heute beginnen wir mit glasfaserverstärkten technischen Kunststoffen PA6, da es sich um die wichtigste Kategorie technischer Kunststoffe PA6 handelt. PA6 hat wie alle anderen technischen Kunststoffe Vor- und Nachteile, wie z. B. eine hohe Wasseraufnahme, Schlagzähigkeit bei niedrigen Temperaturen und eine relativ schlechte Dimensionsstabilität. Daher werden Ingenieure verschiedene Methoden verwenden, um PA6 zu verbessern, was wir Modifikation nennen. Die derzeit gebräuchlichste Methode ist die Mischung und Modifizierung von PA6 mit Glasfasern (GF). Heute werfen wir einen Blick auf die mechanischen Eigenschaften technischer PA6-Kunststoffe unter dem Glasfaser-GF-System als Referenz und helfen uns bei der Materialauswahl. PA6-LGF 1. Einfluss des Glasfasergehalts auf technische PA6-Kunststoffe Wir können anhand der Anwendung und des Experiments feststellen, dass der Inhaltsindex häufig einer der größten Einflussfaktoren bei faserverstärkten Verbundwerkstoffen ist. Mit zunehmendem Glasfaseranteil nimmt die Anzahl der Glasfasern pro Flächeneinheit des Materials zu, was bedeutet, dass die PA6-Matrix zwischen den Glasfasern dünner wird. Diese Änderung bestimmt die Schlagzähigkeit, Zugfestigkeit, Biegefestigkeit und andere mechanische Eigenschaften glasfaserverstärkter PA6-Verbundwerkstoffe. Im Hinblick auf die Schlagzähigkeit wird die Kerbschlagzähigkeit von PA6 durch die Erhöhung des Glasfaseranteils deutlich erhöht. Am Beispiel der Langglasfaserfüllung (LGF) PA6 steigt die Kerbschlagzähigkeit bei einer Erhöhung des Füllvolumens auf 35 % von 24,8 J/m auf 128,5 J/m. Aber der Glasfasergehalt ist nicht besser, das Füllvolumen der kurzen Glasfasern (SGF) erreichte 42 %, die Schlagfestigkeit des Materials erreichte den höchsten Wert von 17,4 kJ/ã¡, aber durch weiteres Hinzufügen wird die Lücke geschlossen Die Schlagfestigkeit zeigte einen Abwärtstrend. In Bezug auf die Biegefestigkeit führt die Erhöhung der Glasfasermenge dazu, dass die Biegespannung zwischen den Glasfasern und der Harzschicht übertragen werden kann. Gleichzeitig absorbiert die Glasfaser, wenn sie aus dem Harz extrahiert oder gebrochen wird, viel Energie und verbessert so die Biegefestigkeit des Materials. Die obige Theorie wird durch Experimente bestätigt. Die Daten zeigen, dass der Biegeelastizitätsmodul auf 4,99 GPa ansteigt, wenn die LGF (Langglasfaser) zu 35 % gefüllt ist. Wenn der Gehalt an SGF (Kurzglasfaser) 42 % beträgt, erreicht der Biegeelastizitätsmodul 10410 MPa, was etwa dem Fünffachen des reinen PA6 entspricht. 2. Einfluss der Glasfaserretentionslänge auf PA6-Verbundwerkstoffe Die Faserlänge der Glasfaser hat offensichtlich auch einen Einfluss auf die mechanischen Eigenschaften des Materials. Wenn die Länge der Glasfaser kleiner als die kritische Länge ist (die Länge der Faser, wenn das Material die Zugfestigkeit der Faser hat), nimmt die Grenzflächenbindungsfläche der Glasfaser und des Harzes mit zunehmender Länge zu die Glasfaser. Beim Brechen des Verbundmaterials ist auch der Widerstand der Glasfasern aus dem Harz größer, so dass die Fähigkeit, der Zugbelastung standzuhalten, verbessert wird. Wenn die Länge der Glasfaser den kritischen Wert überschreitet, kann die längere Glasfaser unter Stoßbelastung mehr Aufprallenergie absorbieren. Darüber hinaus ist das Ende der Glasfaser der Ausgangspunkt für das Risswachstum, und die Anzahl der langen Glasfaserenden ist relativ gering, und die Schlagfestigkeit kann erheblich verbessert werden. Die experimentellen Ergebnisse zeigen, dass die Zugfestigkeit des Materials von 154,8 MPa auf 164,4 MPa steigt, wenn der Glasfaseranteil bei 40 % gehalten wird und die Länge der Glasfaser von 4 mm auf 13 mm zunimmt. Die Biegefestigkeit und die Kerbschlagzähigkeit stiegen um 24 % bzw. 28 %. Darüber hinaus zeigen die Untersuchungen, dass die Materialleistung deutlicher zunimmt, wenn die ursprüngliche Länge der Glasfaser weniger als 7 mm beträgt. Im Vergleich zu kurzen Glasfasern weist mit langen Glasfasern verstärktes PA6-Material eine bessere äußere Verformungsbeständigkeit auf und kann die mechanischen Eigenschaften unter hohen Temperatur- und Feuchtigkeitsbedingungen besser beibehalten. TDS als Referenz PA6 kann zu langglasfaserverstärktem Material verarbeitet werden, indem je nach Produkteigenschaften 20–60 % Langglasfasern hinzugefügt werden. PA6 mit zugesetzten Langglasfasern weist eine bessere Festigkeit, Hitzebeständigkeit, Schlagzähigkeit, Dimensionsstabilität und Verformungsbeständigkeit auf als ohne zugesetzte Glas...

Das Polyamid, das auch unter dem Handelsnamen Nylon bekannt ist, hat hervorragende hitzebeständige Eigenschaften, insbesondere in Kombination mit Additive und Füllstoffmaterialien. Darüber hinaus ist Nylon sehr resistent gegen Abrieb . Xiamen LFT bietet einen weiten Bereich von temperaturresistenten Nylons mit vielen verschiedenen Füllstoffmaterialien .

Polyphthalamid ist a Hochleistungs Harz und Mitglied der Nylon -Familie mit außergewöhnlichen thermischen, mechanischen und physikalischen Eigenschaften Es ist hygroskopisch, undurchsichtig, semikristallin und kann in Plastikinjektionsleisten verwendet werden Die meisten PPA sind gefüllt mit Glasfaser oder Kohlefaser Steifheit bei Hochtemperaturanwendungen zu verbessern Infolgedessen wird PPA häufig in Anwendungen verwendet anstelle von Metall- oder höherpreisiger Thermoplastik.