Polyphenylensulfid ist ein neuer funktioneller technischer Kunststoff.

What is PPS? PPS has a symmetrical rigid backbone and is part of a crystalline polymer consisting of repeated parapplacement of benzene rings and sulfur atoms. PPS are special engineering plastics with high performance, high melting point up to 280℃, which can replace metal. They are located at the top of the polymer property pyramid, as shown in Figure 1. Therefore, based on the excellent performance of PPS resin, make it meet the requirements of harsh engineering plastic projects for materials. Why filling long glass fiber? Long glass fiber reinforced plastic is on the basis of the original pure plastic, adding glass fiber and other additives, so as to improve the scope of use of materials. Advantages: 1. After glass fiber reinforcement, glass fiber is a high temperature resistant material, therefore, the heat resistance temperature of reinforced plastics is much higher than before without glass fiber, especially nylon plastics; 2. After glass fiber reinforcement, due to the addition of glass fiber, limited the mutual movement between polymer chains of plastics, therefore, the shrinkage rate of reinforced plastics decreases a lot, rigidity is greatly improved; 3. After glass fiber reinforcement, the reinforced plastic will not stress crack, at the same time, the anti-impact performance of plastic is improved a lot; 4. After glass fiber reinforcement, glass fiber is a high strength material, which also greatly improves the strength of plastic, such as: tensile strength, compression strength, bending strength, improve a lot; 5. glass fiber reinforced after, due to the addition of glass fiber and other additives, the combustion performance of reinforced plastics decreased a lot, most of the material can not ignite, is a kind of flame retardant material. Datasheets for your reference Zu den Leistungsvorteilen zählen die folgenden Aspekte: ausgezeichnete Hitzebeständigkeit, gute mechanische Eigenschaften, Korrosionsbeständigkeit, selbstflammhemmend bis zur Stufe UL94 V-0. Da PPS die Vorteile der oben genannten Eigenschaften aufweist und im Vergleich zu anderen hochleistungsfähigen thermoplastischen technischen Kunststoffen die Eigenschaften einer einfachen Verarbeitung und niedrigen Kosten aufweist, wird es zu einer hervorragenden Harzmatrix für die Herstellung von Verbundwerkstoffen. Einzelheiten Farbe Original oder nach Bedarf Länge Über 5~24mm Mindestbestellmenge 25kg Paket 25 kg pro Sack Verladehafen Hafen von Xiamen Lieferzeit 7~15 Tage nach Versand

Was ist das PPS? Polyphenylensulfid (PPS) ist ein neues thermoplastisches Harz mit hoher Leistung. Durch die Füllung, modifiziert mit ausgezeichneter Hochtemperaturbeständigkeit, Korrosionsbeständigkeit, Verschleißfestigkeit, Flammschutz, ausgewogenen physikalischen und mechanischen Eigenschaften und ausgezeichneter Dimensionsstabilität und hervorragenden elektrischen Eigenschaften und anderen Eigenschaften des neuen thermoplastischen Hochleistungsharzes sowie hoher mechanischer Festigkeit, chemische Beständigkeit, Flammwidrigkeit, gute thermische Stabilität, hervorragende elektrische Eigenschaften und andere Vorteile. Es hat die Vorteile von hart und spröde, hoher Kristallinität, Entflammbarkeit, guter thermischer Stabilität, hoher mechanischer Festigkeit, hervorragenden elektrischen Eigenschaften, starker chemischer Korrosionsbeständigkeit und so weiter. Die mechanischen Eigenschaften von reinem PPS sind nicht hoch, insbesondere ist die Schlagzähigkeit relativ gering. Gute Kriechfestigkeit unter Belastung, hohe Härte; Hohe Verschleißfestigkeit, der Verschleiß bei 1000 U/min beträgt nur 0,04 g und wird nach dem Einfüllen von F4 und Molybdändisulfid weiter verbessert; Es verfügt auch über einen gewissen Grad an Selbstbefeuchtung. Die mechanischen Eigenschaften von PPS sind weniger temperaturempfindlich. Was ist das PPS-LGF? PPS ist eine der besten hitzebeständigen Sorten im Bereich der technischen Kunststoffe. Die thermische Verformungstemperatur des mit Glasfasern modifizierten Materials liegt im Allgemeinen über 260 Grad und die chemische Beständigkeit ist nach PTFE an zweiter Stelle. Darüber hinaus weist es eine geringe Schrumpfung, eine geringe Wasseraufnahme und eine gute Feuerbeständigkeit auf. Gute Beständigkeit gegen Vibrationsermüdung, starke Beständigkeit gegen Lichtbögen, insbesondere bei hohen Temperaturen. Hervorragende elektrische Isolierung bei hoher Luftfeuchtigkeit. Seine Nachteile sind jedoch Sprödigkeit, Zähigkeit und geringe Schlagzähigkeit. Nach der Modifikation können die oben genannten Mängel behoben und eine sehr hervorragende Gesamtleistung erzielt werden. Als Kunststoff übertreffen seine Eigenschaften und Verwendungsmöglichkeiten die gewöhnlicher Kunststoffe bei weitem und sind in vielerlei Hinsicht genauso gut wie Metallmaterialien. Hervorragendes Material: PPS bietet die Vorteile einer Korrosionsbeständigkeit bei hohen Temperaturen und hervorragender mechanischer Eigenschaften. Es kann Metalle wie Edelstahl, Kupfer, Aluminium, Legierungen usw. ersetzen und gilt als der beste Ersatz für Metall und Kupfer. Was ist die Anwendung von PPS-LGF? PPS wird heute häufig in der Automobil-, Luft- und Raumfahrt-, Haushaltsgeräte-, Maschinenbau- und Chemieindustrie für eine Vielzahl von Strukturteilen, Getriebeteilen, Isolierteilen, korrosionsbeständigen Teilen und Dichtungen verwendet. Unter der Voraussetzung, dass ausreichende Festigkeit und andere Eigenschaften gewährleistet sind, wird das Gewicht des Produkts erheblich reduziert. Datenblatt als Referenz Einzelheiten Nummer Farbe Länge Mindestbestellmenge Paket Probe Lieferzeit Verladehafen PPS-NA-LGF30 Originalfarbe (kann angepasst werden) 5-25mm darüber 25kg 25 kg/Beutel Verfügbar 7-15 Tage nach Versand Xiamen Poer Produktionsprozess _ _ Marken und Zelte _ Teams und Kunden _ Wir bieten Ihnen: 1. Technische Parameter des LFT- und LFT-Materials und Spitzendesign 2. Formfrontdesign und Empfehlungen 3. Bereitstellung technischer Unterstützung wie Spritzguss und Extrusionsformen.

PPS-LCF-Materialien Polyphenylensulfid (PPS) ist ein lineares halbkristallines Polymer mit Benzolring und Schwefelatomen, das aus einer molekularen Hauptkette besteht. Sein Schmelzpunkt liegt bei etwa 280 °C und es weist viele hervorragende Eigenschaften auf, darunter eine Reihe hervorragender Eigenschaften, wie beispielsweise hervorragende mechanische Eigenschaften , chemische Stabilität, Lösungsmittelbeständigkeit, Flammschutzmittel und gute Verarbeitungs- und Formeigenschaften. Als eine Art spezieller technischer Kunststoff mit der derzeit größten Produktion ist die Marktanwendungsgrundlage ausgereift. Darüber hinaus können im Formverfahren Pultrusionsformen, Spritzgießen, Formen und andere Verfahren verarbeitet werden. Durch die Verstärkung von PPS-Harz mit Kohlefasern können hervorragende mechanische Eigenschaften und hitzebeständige Verbundwerkstoffe hergestellt werden. Derzeit werden faserverstärkte PPS-Verbundwerkstoffe häufig in der Luft- und Raumfahrt eingesetzt. Die Tencate Company aus den Vereinigten Staaten verwendet PPS-Harz der Marke Fortron der Ticona Company aus Deutschland, um Kohlefaser-/PPS-Verbundwerkstoffe auf der Grundlage des Gewebe-Heißpressformverfahrens herzustellen. Das Material wird in der Hauptkante der Tragflächen von Airbus A340- und A380-Flugzeugen, in der Querruderstruktur von A340-Flugzeugen, in den Spannungsrippen und Trägern der Fahrwerkstür von Fokker50-Flugzeugen sowie in den Heck-, Ruder- und Höhenruderkomponenten von G650-Geschäftsflugzeugen verwendet. Vorteile Performance characteristics: ◊ receiving aerospace OEM specifications and receiving certification; ◊ excellent cost performance; ◊ Working temperature exceeding Tg according to the design requirements on parts; ◊ laminates can protect against lightning strike and electrochemical corrosion. ◊ inherent flame retardant ◊ excellent chemical stability and solvent resistance; ◊ Long-term storage at ambient temperature. Main applications: ◊ Major and minor aircraft structures: ◊ wing leading edge, engine tower, body splint structure, etc. ◊ aircraft interior structure: ◊ seat structure parts, trunk, etc ◊ On specific requirements on corrosion resistance, dimensional stability, and shock absorption on high-end industrial areas Application Production process Our team and customers Come and contact us!

PPS The molecular structure of PPS consists of benzene ring and sulfur atoms interarranged, the configuration is orderly, easy to form a high thermal stability of the crystal structure. At the same time, the molecular structure of PPS material has a highly stable chemical bond characteristics, the benzene ring structure makes PPS more rigid, and the sulfur ether bond (-S-) provides a certain degree of flexibility. PPS itself has good heat resistance, flame retardant, chemical resistance, should be a promising material, but unmodified PPS has some unavoidable defects: Difficult processing:  This is the biggest pain point of all high temperature resistant materials -- high processing temperature, no matter the molding process or processing energy consumption, will face great challenges. In addition, PPS is still prone to thermal oxidation crosslinking in the melting process, resulting in reduced fluidity and further improve the processing difficulty; Poor toughness: PPS molecular chain is rigid, the maximum crystallinity is as high as 70%, the elongation is low and the welding strength is not so good. As a result, the impact resistance of unmodified PPS is poor, which limits the application scope. High cost: PPS raw materials and general engineering plastics compared, the price is about 1-2 times higher, and some modified materials compared with low cost performance; Difficult coating: PPS surface coating and coloring performance is not ideal. While this is not a major problem for now, it is a limiting factor. PPS-LGF Long glass fiber reinforced composites can solve your problems when other methods of reinforced plastics do not provide the performance you need or if you want to replace metal with plastic. Long glass fiber reinforced composites can cost-effectively reduce the cost of goods and effectively improve the mechanical properties of engineering polymers, and increase the durability by forming long fibers to form a long-fiber-reinforced internal skeleton network. Performance is preserved in a wide range of environments. TDS als Referenz Anwendung Über uns Xiamen LFT Composite Plastic Co., Ltd. ist ein Markenunternehmen, das sich auf LFT&LFT konzentriert. Langglasfaser-Serie (LGF) und lange Carbonfaser-Serie (LCF). Der thermoplastische LFT kann für das Spritzgießen und Extrudieren von LFT-G sowie für das Formen von LFT-D verwendet werden. Es kann nach Kundenwunsch hergestellt werden: 5~25 mm Länge. Die langfaserigen, durch kontinuierliche Infiltration verstärkten Thermoplaste des Unternehmens haben die Systemzertifizierung nach ISO9001 und 16949 bestanden und die Produkte haben zahlreiche nationale Marken und Patente erhalten.

PPS Spezielle technische Kunststoffe sind technische Kunststoffe mit höherer Gesamtleistung und langfristiger Einsatztemperatur über 150℃, PPS ist einer davon. Die kohlenstofffaserverstärkten speziellen technischen Verbundwerkstoffe, die aus Kohlenstofffasern als Verstärkung und diesen speziellen technischen Kunststoffen als Matrix bestehen, weisen hervorragende mechanische Eigenschaften, Verschleißfestigkeit und hohe Temperaturbeständigkeit auf und können in den Bereichen Luft- und Raumfahrt, Schifffahrt oder Medizin sowie in einigen Aspekten eingesetzt werden zeigen wünschenswertere Anwendungsvorteile als duroplastische Harze oder sogar Metallmaterialien. PPS-LCF Die Festigkeit und Härte des Polyphenylensulfid-PPS-Harzes ist relativ hoch, die mechanischen Eigenschaften sind gut, es passt sich einer Vielzahl von Form- und Verarbeitungsmethoden an, Sie können ein sekundäres Präzisionsformen erreichen, die Dimensionsstabilität des Produkts ist besser. Die Feuchtigkeitsaufnahme beträgt nur 0,03 %, die Dichte ist niedrig, die Schmelztemperatur Tm beträgt 285 °C, die Glasübergangstemperatur Tg beträgt 90 °C, die thermische Stabilität ist sehr gut, im Luftzustand erreicht sie 430 °C bis 460 °C vor der Zersetzung, hoch Flammhemmender Grad, 200 ℃ unlöslich in den meisten organischen Lösungsmitteln, ausgezeichnete elektrische Isolierung. Als spezieller technischer Kunststoff weist PPS herausragende Vorteile auf, weist jedoch auch Nachteile auf, beispielsweise aufgrund der großen Anzahl an Benzolringen, die seine Schlagfestigkeit und Dehnung nicht gut genug machen, aber durch die kohlenstofffaserverstärkte Art und Weise, Durch den kohlenstofffaserverstärkten Eingriff, der die ursprünglichen Isoliereigenschaften von PPS in leitfähige, antistatische Eigenschaften umwandelt, können die Zähigkeit und Festigkeit von Polyphenylensulfid-PPS erheblich erhöht und verbessert werden, wodurch es zu einem der am häufigsten verwendeten Verbundwerkstoffe in der Luft- und Raumfahrt wird. Es wird in Flugzeugfahrwerken, Flügeln, Luken, Treibstofftank-Anschlussabdeckungen, J-förmigem Bugkegel, Kabineninnenverkleidungen und anderen Komponenten verwendet, um nicht nur die Schlagfestigkeit, Hochtemperatur- und Korrosionsbeständigkeit dieser Teile zu erhöhen, sondern auch durch die Reduzierung der Masse, um die Auslastungseffizienz des Flugzeugs zu verbessern und den Treibstoffverbrauch zu senken. Im Vergleich zu Metall bietet dieser Verbundwerkstoff die Vorteile geringer Kosten und einfacher Verarbeitung, die Kosten können um 20-50 Prozent gesenkt werden. Zwischen der Kohlefaserverstärkung und der PPS-Harzmatrix muss eine hohe Bindung aufrechterhalten werden. Wenn das Produkt einer Belastung ausgesetzt ist, trägt diese hohe Bindung dazu bei, dass die Grenzfläche die äußere Belastung effektiv auf die Fasern überträgt, wodurch wirksam verhindert werden kann, dass sich Risse zwischen den Grenzflächen lösen, und außerdem werden die mechanischen Eigenschaften des Verbundwerkstoffs verbessert. Um zwischen der Harzmatrix und der Kohlefaserverstärkung eine hohe Bindung zu bilden, müssen wir den geschmolzenen Zustand des PPS-Harzes und der Kohlefaserverstärkung in vollständigen Kontakt bringen und vollständig imprägnieren, damit der Faserkörper im Falle einer gleichmäßigen Dispersion eine gute Wirkung erzielt Imprägnierungseffekt. Fertigungsprozess Anwendung von PPS-LCF Xiamen LFT Verbundkunststoff Co., Ltd Wir bieten Ihnen: 1. Technische Parameter des LFT- und LFT-Materials und Spitzendesign 2. Formfrontdesign und Empfehlungen 3. Bereitstellung technischer Unterstützung wie Spritzguss und Extrusionsformen. Über uns

Polyphenylene sulfide PPS is one of the typical representatives of special engineering plastics, with a linear structure of alternating benzene rings and sulfur atoms. In the condensed structure, PPS is easy to crystallize, crystallinity of nearly 70%, therefore, has good thermal stability, chemical stability and dimensional stability, etc. PPS mainly has the following five performance advantages. (1) excellent heat resistance. pps melting point of more than 280 ℃, heat deflection temperature of more than 260 ℃, and after high-temperature heat aging treatment, the strength retention rate is high. (2) since the flame retardant. PPS itself has flame retardant, without adding flame retardants flame retardant level can reach UL94 V- 0 level. (3) good mechanical properties. PPS is a brittle material, has good creep resistance, high surface hardness, good wear resistance, and carbon fiber and other materials compound, but also shows good self-lubricating properties. (4) excellent chemical resistance, irradiation resistance. pps below 200 ℃ almost insoluble in any solvent, can withstand almost all inorganic substances, radiation dose up to 108Gy. (5) good processing properties. pps melt viscosity is low, as the resin matrix of composite materials, for the reinforcement of the flow of excellent wetting effect. As PPS has the above performance advantages, and compared to other high-performance thermoplastic resins and easy processing, low cost, so become an excellent resin matrix for the manufacture of composite materials. Long glass fiber Glass fiber is an inorganic non-metallic material with excellent performance, is a natural mineral with silica as the main raw material, add specific metal oxide mineral raw materials, mixed evenly, molten at high temperature, molten glass liquid flow through the funnel outflow, in the role of high-speed pull gravitational force is drawn and rapidly cooled and cured into a very fine continuous fiber. Glass fiber monofilament diameter from a few microns to more than twenty microns, equivalent to a hair of 1/20-1/5, each bundle of fiber original filament are composed of hundreds or even thousands of monofilaments. Glass fiber basic properties: The appearance of a smooth cylindrical surface, the cross-section is a complete circle, round cross-section to withstand the load capacity; gas and liquid through the resistance is small, but the surface is smooth so that the holding force of the fiber is small, not conducive to the combination with the resin; density is generally in 2.50-2.70 g/cm3, depending mainly on the glass composition; tensile strength than other natural fibers, synthetic fibers to be high; brittle materials, the elongation at break is very small ; water resistance and acid resistance is good, while alkali resistance is poor. It can be divided into continuous glass fiber, short glass fiber (SGF) and long glass fiber (LGF) by length classification. Long glass fiber is the most widely used glass fiber at present. And Xiamen LFT plastic composite company is focuses on the produce of long glass fiber compounds for many years. SGF VS LGF 1. The difference in size length Engineering materials long glass fiber and short glass fiber, literally means the difference in size length; more common short glass fiber size is about 0.2mm-0.6mm between; long glass fiber size is about 6mm-25mm between. 2. Performance strength differences Different lengths of glass fibers are different in their performance strength, the fiber length of long glass fibers in the composite material inside the impact strength than short glass fibers stronger. 3. Production process is different Production of long glass fiber, high requirements for raw materials, especially the manufacturing process requires the surface of glass fiber to be activated, the processing can not be flooded with glass fibers, as well as external leakage phenomenon occurs. Production of short glass fiber, because the size is generally no special requirements, so the production is relatively easy, the requirements for raw materials are not so high, the production costs for manufacturers low. 4. Different production and processing methods Long glass fiber production and processing methods generally use injection molding and molding; while most short glass fiber injection molding method. Product process TDS for reference only Details Number Color Length Sample Packing MOQ Port of Loading Delivery time PPS-NA-LGF40 Originalfarbe (oder nach Bedarf ) 12 mm (oder nach Bedarf) Verfügbar 25 kg/Beutel 25kg Hafen von Xiamen 7~15 Tage nach Versand Warum uns wählen 1. Technische Parameter des LFT- und LFT-Materials und Spitzendesign 2. Formfrontdesign und Empfehlungen 3. Bieten Sie technische Unterstützung wie Spritzguss und Extrusionsformen.

PPS-Informationen Polyphenylensulfid (PPS) wird vor der Modifizierung nicht verbessert, seine Nachteile sind Sprödigkeit, schlechte Zähigkeit, geringe Schlagzähigkeit, nach dem Füllen werden Glasfasern, Kohlefasern und andere Verbesserungen modifiziert, um die oben genannten Mängel zu überwinden und eine sehr gute Gesamtleistung zu erzielen. PPS-Füllung. Lange Kohlefaser In der Industrie für modifizierte technische Kunststoffe sind langfaserverstärkte Verbundwerkstoffe Verbundwerkstoffe, die durch eine Reihe spezieller Modifizierungsverfahren aus langen Kohlenstofffasern, langen Glasfasern und einer Polymermatrix hergestellt werden. Das wichtigste Merkmal von Langfaserverbundwerkstoffen ist, dass sie über eine überlegene Leistung verfügen, die die Originalmaterialien nicht bieten. Wenn wir sie nach der Länge der hinzugefügten Verstärkungsmaterialien klassifizieren, können sie in Langfaser-, Kurzfaser- und Endlosfaserverbundstoffe unterteilt werden. Lange Kohlefaserverbundwerkstoffe sind eine Art langfaserverstärkter Verbundwerkstoffe, bei denen es sich um ein neues Fasermaterial mit hoher Festigkeit und hohem Modul handelt. Es handelt sich um einen neuen Werkstoff mit hervorragenden mechanischen Eigenschaften und vielen Sonderfunktionen. Korrosionsbeständigkeit: LCF-Kohlenstofffaserverbundwerkstoffe weisen eine gute Korrosionsbeständigkeit auf und können sich an die raue Arbeitsumgebung anpassen. UV-Beständigkeit: Die UV-Beständigkeit ist stark und die Produkte werden durch UV-Strahlung weniger geschädigt. Abrieb- und Schlagfestigkeit: Der Vorteil im Vergleich zu allgemeinen Materialien liegt auf der Hand. Geringe Dichte: geringere Dichte als viele Metallmaterialien, kann den Zweck eines geringen Gewichts erreichen. Weitere Eigenschaften: Reduzierung des Verzugs, Verbesserung der Steifigkeit, Schlagzähigkeit, Erhöhung der Zähigkeit, elektrische Leitfähigkeit usw. LCF-Kohlenstofffaserverbundwerkstoffe weisen im Vergleich zu Glasfasern eine höhere Festigkeit, höhere Steifigkeit, ein geringeres Gewicht und eine hervorragende elektrische Leitfähigkeit auf. PPS TDS als Referenz PPS-Anwendung Für weitere technische Beratung können Sie sich auch an uns wenden. Fragen und Antworten 1. Sind Kohlefaserverbundprodukte sehr teuer? Der Preis von Kohlefaserverbundprodukten hängt eng mit dem Rohstoffpreis, dem Technologiestand und der Anzahl der Produkte zusammen. Je höher die Leistung des Rohmaterials, desto teurer ist es, beispielsweise das in der Orthopädie verwendete thermoplastische Carbonfaser-PEEK-Material. Je komplexer der Herstellungsprozess, desto höher sind natürlich die Arbeitszeit und der Arbeitsaufwand sowie die Produktionskosten. Allerdings gilt: Je größer die Bestellmenge, desto geringer sind die Kosten pro Produkt. Auf lange Sicht verlängert die überlegene Leistung von Kohlefaser die Lebensdauer des Produkts, verringert die Anzahl der Wartungsarbeiten und trägt auch sehr dazu bei, die Nutzungskosten zu senken. 2. Sind Kohlefaserverbundprodukte giftig? Kohlefaserverbundwerkstoffe bestehen aus Kohlefaserfilamenten, die mit Keramik, Harzen, Metallen und anderen Substraten gemischt sind, und sind im Allgemeinen nicht toxisch. Beispielsweise besteht das oben erwähnte PEEK-Material aus lebensmittelechtem Harz, das sehr gut mit dem menschlichen Körper kompatibel und nicht nur für den Menschen ungefährlich ist, sondern aufgrund seiner hohen Festigkeit und Elastizität auch ein idealeres Material für orthopädische Chirurgie darstellt Modul in der Nähe der Knochenrinde. Die medizinische Bettplatte aus Kohlefaser steht im täglichen Kontakt mit dem Körper vieler Patienten und hat keine negativen Auswirkungen auf den menschlichen Körper. Im Gegenteil, sie sorgt für die Genauigkeit der medizinischen Diagnose und ist eine große Hilfe. 3. Was ist der Unterschied zwischen duroplastischen Carbonfaser-Verbundwerkstoffen und thermoplastischen Carbonfaser-Verbundwerkstoffen? Duroplastische Kohlefaserverbundwerkstoffe begünstigen die Rolle des Härters beim Aushärten und Formen. Während thermoplastische Kohlefaserverbundprodukte hauptsächlich auf Abkühlung angewiesen sind, um die Formgebung zu erreichen. Thermoplastische Kohlefaserverbundwerkstoffe erfreuen sich nicht so großer Beliebtheit wie duroplastische Kohlefaserverbundwerkstoffe, vor allem weil sie teuer sind und im Allgemeinen in High-End-Industrien eingesetzt werden. Duroplastische Kohlefaserverbundstoffe sind aufgrund der Beschränkung der Harzmatrix selbst schwer zu recyceln und werden im Allgemeinen nicht in Betracht gezogen; Thermoplastische Kohlefaserverbundwerkstoffe können recycelt werden und können doppelt so lange hergestellt werden, wenn sie auf eine bestimmte Temperatur erhitzt werden. Über uns Wir bieten Ihnen: 1. Technische Parameter des LFT- und LFT-Materials und Spitzendesign 2. Formfrontdesign und Empfehlungen 3. Bereitstellung technischer Unterstützung wie Spritzguss und Extrusionsformen

PPS-Material In den letzten Jahren hat sich die Anwendung spezieller technischer Kunststoffe schrittweise von den früheren Bereichen Militär und Luft- und Raumfahrt auf immer mehr zivile Bereiche ausgeweitet, beispielsweise in der Automobilindustrie, im Gerätebau, bei hochwertigen Konsumgütern usw. Darunter ist Polyphenylensulfid (PPS). ) und Polyetheretherketon (PEEK) sind zwei spezielle technische Kunststoffe, die sich relativ schnell entwickelt haben und ein breites Anwendungsspektrum haben. PEEK ist PPS hinsichtlich Festigkeit, Zähigkeit und maximaler Betriebstemperatur überlegen. Hinsichtlich der Hochtemperaturbeständigkeit ist PEEK etwa 50 °C höher als PPS. Andererseits führen die relativ offensichtlichen Kostenvorteile und besseren Verarbeitungseigenschaften von PPS zu einer größeren Verbreitung. PPS ist ein kristallines, hochsteifes weißes Pulverpolymer mit hoher Hitzebeständigkeit (langfristiger Einsatz von 200 °C bis 220 °C, kurzfristig hohe Temperaturen von 260 °C), mechanischer Festigkeit, Steifigkeit, Flammschutz und chemischer Beständigkeit , elektrische Eigenschaften, Dimensionsstabilität sind ausgezeichnete Harze. Es verfügt über eine ausgezeichnete Verschleißfestigkeit, Kriechfestigkeit, Flammhemmung und selbstverlöschende Eigenschaften. Es behält gute elektrische Eigenschaften bei hoher Temperatur und hoher Luftfeuchtigkeit. Gute Fließfähigkeit, leicht zu formen, fast keine Schrumpfung und konkave Stelle beim Formen. Gute Affinität zu verschiedenen anorganischen Füllstoffen. Es wurde entwickelt, um den Unterschied zwischen standardmäßigen thermoplastischen Materialien (z. B. PA, POM, PET ...) und fortschrittlichen technischen Kunststoffen zu verkürzen. PPS bietet die folgenden deutlichen Leistungsvorteile: (1) Von Natur aus flammhemmend Im Gegensatz zu PC und PA sind reines PPS-Harz und seine mit Glasfasern/Mineralpulver gefüllten Verbundwerkstoffe ohne zusätzliche Flammschutzmittel erhältlich. Obwohl PC und PA einen günstigeren Preis und eine bessere mechanische Festigkeit (insbesondere Schlagzähigkeit) als PPS haben, sind die Kosten für PC- und PA-Verbundwerkstoffe mit Zusatz von halogenfreien Flammschutzformulierungen (V-0@0,8 mm²) deutlich höher. in vielen Fällen sogar höher als bei PPS-Materialien mit gleicher mechanischer Festigkeit. (2) Ultrahohe Fließfähigkeit Beim teilkristallinen PPS kann aufgrund seiner sehr hohen Fließfähigkeit eine Glasfaserfüllung von problemlos mehr als 50 % erreicht werden, während im Prozess der Hochtemperatur-Schmelzmischungsextrusion die geringere Viskosität von PPS im Vergleich zu PC dazu führen kann, dass die Glasfasern einem geringeren Grad standhalten von Scherung und Extrusion, so dass die endgültigen Spritzgussprodukte eine längere Retentionslänge haben, um den Effekt des Moduls weiter zu verbessern. (3) Extrem geringe Wasseraufnahme Dieser Vorteil gilt hauptsächlich für PA. Hinsichtlich der Fließfähigkeit sind hochgefüllte PA und PPS vergleichbar; und für die mechanischen Eigenschaften ist die gleiche Menge an füllenden PA-Verbundwerkstoffen vorteilhafter. Zusätzlich zu den Einschränkungen hinsichtlich der halogenfreien Flammschutzmittel ist die hohe Wasseraufnahme von PA ein weiterer Faktor, der die Anwendung einschränkt: Im Vergleich zu Hochtemperatur-Nylon PA6T ist die Wasseraufnahme von 0,6–1 % bei PPS mit 0,03 % nahezu vernachlässigbar. Das Ergebnis ist, dass bei PPS-Produkten aufgrund der Wasseraufnahme und Verformung die Produktfehlerrate viel geringer ist als bei PA-Produkten unter den gleichen Bedingungen. (4) die einzigartige metallische Textur und die höhere Oberflächenhärte PPS-Spritzgussteile fallen auf den Tisch, ein sehr knackiges Geräusch, das nur beim PPS-Absturz zu hören ist. Durch die spezielle Form und die angemessene Formtemperatur klingen die PPS-Spritzgussteile bei menschlicher Berührung auch ähnlich wie der Aufprall von Metall, die Oberfläche ist spiegelglatt und hat einen metallähnlichen Glanz. PPS-LCF-Verbindungen Länge: ca. 12 mm, oder kundenspezifisch Farbe: Originalfarbe oder individuell Faserspezifikation: 20 % - 60 % Note: Allgemeine Note Mit langen Kohlenstofffasern verstärkte Verbundwerkstoffe bieten erhebliche Gewichtseinsparungen und sorgen für optimale Festigkeits- und Steifigkeitseigenschaften in verstärkten Thermoplasten. Die hervorragenden mechanischen Eigenschaften von mit langen Kohlenstofffasern verstärkten Verbundwerkstoffen machen sie zu einem idealen Ersatz für Metalle. In Kombination mit den Design- und Fertigungsvorteilen spritzgegossener Thermoplaste vereinfachen lange Kohlefaserverbundwerkstoffe die Neugestaltung von Komponenten und Geräten mit anspruchsvollen Leistungsanforderungen. Aufgrund seiner weit verbreiteten Verwendung in der Luft- und Raumfahrt und anderen fortschrittlichen Industriezweigen wird es von den Verbrauchern als „Hightech“ wahrgenommen. Datenblatt als Referenz Anwendung Fabrik Fragen und Antworten 1. Gibt es einheitliche Referenzdaten für die Leistung von Kohlefaserprodukten? Di...

Polyamid 12-Füllung mit Langglasfaser Die empfohlene Langzeitarbeitstemperatur von Polyphenylensulfidharz (PPS) beträgt 220–240 °C. Das Material verfügt über eine gute thermische Stabilität und seine mechanischen Eigenschaften bleiben bei 100 °C, 160 °C und 200 °C bei etwa 80 % bzw. 60 % ihrer ursprünglichen Werte. Das Material weist bei Raumtemperatur eine ausgezeichnete Kriechfestigkeit und Ermüdungsbeständigkeit auf. Das Material verfügt außerdem über eine ausgezeichnete Beständigkeit gegenüber Säuren, Laugen, Salzen, organischen Lösungsmitteln und anderen Medien, mit Ausnahme von oxidierenden Säuren und stark oxidierenden Medien, und ist in allen chemischen Lösungsmitteln unter 170 °C nahezu unlöslich. Es eignet sich besonders für die Korrosionsbeständigkeit von Flusssäure, halogenierten Kohlenwasserstoffen und Chloridionen. PPS ist ein flammhemmendes Material mit einem Sauerstoffindex von 46 bis 53, besser als die meisten technischen Kunststoffe. Polyphenylensulfid weist einen hohen Widerstand und eine niedrige Dielektrizitätskonstante auf und kann unter Bedingungen hoher Temperatur und hoher Luftfeuchtigkeit gute elektrische Eigenschaften beibehalten. Darüber hinaus sind die mechanischen Eigenschaften des Harzmaterials nicht sehr herausragend, da es eine gute Affinität zu Glasfasern, Kohlenstofffasern, anorganischen Füllstoffen und Festschmierstoffen aufweist und die Modifikation gut ist, sodass die beim Spritzgießen verwendeten Partikel hauptsächlich modifiziert und verstärkt werden durch verschiedene Fasern und anorganische Füllstoffe. LGF und SGF Nylonpartikel aus gewöhnlichen Glasfasern: Die Größe beträgt etwa 3 bis 4 mm, das Verhältnis von Länge zu Breite beträgt 50 bis 250. Nylonpartikel aus langen Glasfasern: Die Größe beträgt etwa 10 bis 12 mm und das Seitenverhältnis > 400. Darüber hinaus ist die Verteilung der Glasfasern in den beiden Auch die Art der Teilchen ist unterschiedlich. Im Vergleich zu SGF weist LGF eine verbesserte Steifigkeit, Festigkeit und einen höheren Modul auf, insbesondere wurde die Kerbschlagzähigkeit erheblich verbessert. Im Vergleich zu SGF weist LGF eine verbesserte Steifigkeit, Festigkeit und einen höheren Modul auf, insbesondere wurde die Kerbschlagzähigkeit erheblich verbessert. Die Steifigkeitserhaltungsrate von Langglasfasern ist besser als die von Kurzglasfasern, und Langglasfasern sind widerstandsfähiger gegen Wärmealterung. Die Kriechleistung wird durch Zeit, Temperatur und Belastung beeinflusst. Bei 120 °C und einer Belastung von 40 MPa ist das Kriechen von Langglasfasern deutlich besser als das von Kurzglasfasern. Dies ist von entscheidender Bedeutung für Teile mit langfristigem statischem Druck, und lange Glasfasern können ausprobiert werden, wenn kurze Glasfasern die Anforderungen nicht erfüllen können. Die Schrumpfung ist entscheidend für die Größe des Teils. Die Querschrumpfung von Kurzglasfasermaterial ist viel höher als die Längsschrumpfung, und die Anisotropie ist schwerwiegender, was zu einer schwierigen Kontrolle der Teilegröße und einer offensichtlichen Schrumpfung führt. Im Gegensatz dazu liegen die Schrumpfungsraten in Quer- und Längsrichtung von Langglasfasermaterialien sehr nahe beieinander, was eine Isotropie zeigt, was das Risiko eines Teileverzugs erhöht und die Abmessungen besser kontrollierbar macht. Produktprozess Zertifizierung Zertifizierung des Qualitätsmanagementsystems ISO9001/16949 Nationales Laborakkreditierungszertifikat Innovationsunternehmen für modifizierte Kunststoffe Ehrenurkunde Schwermetall-REACH- und ROHS-Prüfung Über uns Xiamen LFT Composite Plastic Co. , Ltd. ist ein Markenunternehmen, das sich  auf  LFT&LFT konzentriert. Langglasfaser-Serie (LGF ) und lange Carbonfaser-Serie (LCF ). Der thermoplastische LFT des Unternehmens kann für das Spritzgießen und Extrudieren von LFT-G sowie für das Formen von LFT-D verwendet werden. Es kann nach Kundenwunsch hergestellt werden:  5~25 mm Länge. Die langfaserigen, durch kontinuierliche Infiltration verstärkten Thermoplaste des Unternehmens haben die Systemzertifizierung nach ISO9001 und 16949 bestanden und die Produkte haben zahlreiche nationale Marken und Patente erhalten.  Hauptprodukte